Owned by: China Association for Science and Technology
Sponsored by: China Coal Society
Published by: Springer Nature
About issue

The International Journal of Coal Science & Technology is a peer-reviewed open access journal. It focuses on key topics of coal scientific research and mining development, serving as a forum for scientists to present research findings and discuss challenging issues.


Coverage includes original research articles, new developments, case studies and critical reviews in all aspects of scientific and engineering research on coal, coal utilizations and coal mining. Among the broad topics receiving attention are coal geology, geochemistry, geophysics, mineralogy, and petrology; coal mining theory, technology and engineering; coal processing, utilization and conversion; coal mining environment and reclamation and related aspects.


The International Journal of Coal Science & Technology is published with China Coal Society, who also cover the publication costs so authors do not need to pay an article-processing charge.


The journal operates a single-blind peer-review system, where the reviewers are aware of the names and affiliations of the authors, but the reviewer reports provided to authors are anonymous.


  • A forum for new research findings, case studies and discussion of important challenges in coal science and mining development

  • Offers an international perspective on coal geology, coal mining, technology and engineering, coal processing, utilization and conversion, coal mining environment and reclamation and more

  • Published with the China Coal Society

Show More
Editors-in-Chief
Suping Peng, Shimin Liu
Managing Editor
Wanjie Wang
Associate Editors
Bo Hyun Kim, Dongjie Xue, Pedram Roghanchi, Wu Xiao, Zhiqiang Wu
Publishing model
Open Access. Learn about publishing OA with us
Home > Volumes and issues > Volume 2, issue 1

Optical microscopy analysis of briquette binders

Research Article

Open Access

Published: 10 March 2015

0 Accesses

International Journal of Coal Science & Technology Volume 2, 421-427, (2015)

Abstract

Environmental requirements and demands from the coal industry have resulted in a boom in briquetting technology in China. In this work, a low-volatility bituminous coal from the Changcun mine and bentonite binders are used for briquetting. The compressive strength, impact strength, and thermal stability of briquettes made using different binder concentration are determined. The morphology and distribution of binders in briquettes are studied by optical microscopy and digital image-processing technologies. The concept of roundness is introduced to indicate the pressure to which the binders are subjected during briquetting. The influences of binder morphology on briquette strength are discussed. The binders are mainly in aggregated and dispersed forms, present in similar proportions in the briquettes. Aggregated binders with large differences in size are not well-distributed. Binder roundness values are concentrated between 1.5 and 4.0, which indicates that most aggregated binders are compressed and conform well to the surfaces of coal particles. A few binders had roundness value approximating 1 or above 4, which indicated that these were under little pressure or overloaded, respectively. The relationships between briquette strength and binder morphology show that aggregated binders are detrimental to mechanical strength while dispersed binders benefit briquetting.

1.Introduction

In 2013, 3.7 billion tons of coal sample were mined and 3.61 billion tons of coal were consumed in China. Coal accounted for about 65.7 % of China’s primary energy in 2013 and is anticipated to remain the primary energy source well into the future. As more emphasis is placed on cleaner production and controlling air pollution, cleaner utilization of coal is a strong direction of future development. The use of briquettes instead of raw coal can reduce pollutant missions and alleviate haze in coal combustion. For example, briquettes made of anthracite are recommended for heating in areas surrounding Beijing. Furthermore, applications of fixed-bed gasification technologies have increased rapidly, as have developments in coal-to-oil and coal-to-natural gas technologies. Briquetting is an effective way of supplying the gasification feedstock and improving economic efficiency.

Strength of the briquettes is the primary issue to be considered in briquette manufacture, but the intrinsic factors affecting the strength of briquettes have not been well researched, although relationships between structure and properties are the core of modern materials science. During assembling the components of materials, the macroscopic properties of the material are well known to be dominated by its microstructure (Olson 1997; Nan 2005). Research concerning relationships between the microstructure and the macroscopic properties is necessary to model and improve the performances of materials.

The performance of binders is crucial in the briquetting of pulverized coal using medium or low pressures (Xu and Liu 2001), especially for high quality coal. As important microstructural characteristics, the morphology and distribution of the binders have a strong effect on their performance. In this study, the microstructures (morphology and distribution) of binders in briquettes and their influence on briquette strength are discussed.

There are a variety of approaches for microstructure observation, which can be divided into direct and indirect observation methods (Xu 2011). Optical microscopy, stereo microscopy, and scanning electron microscopy are commonly used methods of direct observation, while nondestructive methods based on interferometry, acoustic emission, and X-ray computed tomography are the main methods of indirect observation (Mehta and Monteiro 2006). Optical microscopy is widely used in quality assessment of raw materials and products, defect inspection, and design of new materials in the fields of rock mechanics, metallurgy, silicates (ceramics, cement), sintered minerals, composite materials, biology, and medicine. The morphology and distribution of binders in briquettes can also be characterized by optical microscopy. Binder microstructures can also be accurately measured by digital image-processing technology, which has seen rapid development and application in recent years. In this work, optical microscopy and digital processing technology were chosen to study the binder microstructures in the briquettes.

2.Experimental

A low-volatility bituminous coal from Changcun mine, Shanxi Province, was employed, and the compositional and chemical analyses of which are presented in Tables 1 and 2. The coal was pulverized in a hammer crusher. The particle size distribution after crushing is given in Table 3. Table 4 shows the analysis of the bentonite chosen as the binder for briquetting. Montmorillonite is the main mineral component of the bentonite (Jiang and Zhang 2005). As a common binder for briquetting, the bentonite is obvious in optical microscopy and can be easily distinguished from the pulverized coal particles and clay minerals in polished sections, which makes it a perfect binder for this study. The bentonite particle size was <149 µm (100 mesh).

Table 1 Compositional analysis of feed coal
 

Air dried (%)

Dried (%)

Moisture

1.48

 

Ash

 

19.97

Volatile

 

11.89

Fixed carbon

 

68.14

Table 2 Chemical analysis of feed coal
 

Dry ash-free basis (%)

Carbon

90.37

Hydrogen

4.12

Nitrogen

3.53

Sulfur

1.53

Oxygen

0.45

Table 3 Particle size distribution of feed coal

Size distribution (mm)

Mass fraction (%)

>3

1.5

2–3

12.4

1.5–2

10.7

1–1.5

0.8

0.5–1

24.5

<0.5

50.1

Table 4 Analysis of bentonite

Moisture (air dried, %)

6.28

Ash (dry, %)

95.15

SiO2 (%)

58.01

Al2O3 (%)

14.34

K + Na (%)

1.46

Weight loss at high temperature (%)

10.54

2.1 Preparation of the briquettes

The briquetting mold was a cylinder of 40 mm diameter and 25 mm height. Briquetting was carried out using a MJTY (MSY)-58T hydraulic molding machine at a briquetting pressure of 12 MPa. Binder concentrations of 3 %, 5 % , 7 % , and 9 % were studied. All constituents were measured in weight percent. The feed coal particles and the binders were stirred for 5 min. After these components were fully mixed, water was introduced to give a briquette moisture content up to 12 % (dry basis of feed coal). The coal/binder mixtures added into the mold were limited to (30 ± 0.2) g to eliminate the influence of mass difference on the briquette strength (Richards 1990). The green briquettes were placed in an oven at 105 °C for 3 h to produce the product briquettes. Compressive strength (measured according to Chinese Standard MT/T 748-2007, 2007), impact strength (MT/T 925-2004, 2004b), and thermal stability (MT/T 924-2004, 2004a) were then determined for each group of briquettes.

2.2 Observations of the binders in briquettes

The observations of the binders were carried on polished sections of the briquettes, prepared using the boiling-rosin method for lump coal specimens, according to Chinese Standard GB/T 16773-2008 (2008). The numbers of specimens required to obtain representative values for quantitative analyses were selected according to Stach et al. (1982). Two polished sections were made for each group of briquettes. The longitudinal section of the briquettes was parallel with the compression direction during briquetting while the cross-section was vertical to the direction of compression.

Microstructural observations were conducted using a Zeiss™ Axioskop 40 polarizing microscope and images of the binders were taken using a CoolSnap™ microscopic digital camera. Quantitative determination of the binders was conducted according to Chinese Standard GB/T 8899-1998. The coordinates of the central point of each binder particle were recorded in a two-dimensional coordinate system established by ProScan™ software. The objective magnifications were 5 or 10 times and the eyepiece magnifications were 10 times. The binder particles were observed using ×10 objectives. When the binder sizes were beyond the field of vision, a ×5 objective was used. The morphological parameters, such as binder area, were determined by image processing software. Distribution diagrams were drawn using the coordinate values of the central points and the binder areas.

3.Results and discussion

3.1 Morphology and distribution of binders

Two forms of binders were found in the briquettes examined by optical microscopy. The binder was either agglomerated with the coal particles (Fig. 1a) or dispersed in the coal/binder matrix mixture (Fig. 1b). To enable bentonite to be used as the binder, grinding was required, which dramatically increased the surface area and electrified the particles. The charge force (Zeng et al. 2001) and surface tension (Liu et al. 2001) both contribute to agglomeration of the fine bentonite particles, some of which disperse in the matrix of the coal/binder mixture during the stirring and mixing steps of briquette preparation.

Fig. 1
figure 1

Morphology of binders in briquettes. a Alomerated binder (reflected light, air, polarized light, ×100). b Dispersed binder (reflected light, air, crossed polar, ×200)

Small particles and dark colors were seen in the dispersed binders, which made quantitative analysis difficult, so this study focused on agglomerated binders. The binder addition was measured as the mass fraction per dry basis of the feed coal. The quantitative results from microscopic analysis are presented as units of volume fraction. The conversion of mass fraction to volume fraction is as follows:

$$V = \frac{x/2.68}{x/2.68 + 100/1.46} \times 100\%$$

where V is the volume fraction of binders (%); x is the binder concentration (mass fraction, %).

Note: The true relative densities (TRD) of the bentonite and feed coal used in this study are 2.68 and 1.46, respectively.

True relative density was determined according to Chinese Standard GB/T 217-2008.

The volume fractions of detected binders are shown in Table 5. The volume determinations of briquettes made with 3 % binder were based on the cross section. The binders in briquettes behave similarly to macerals in coal, so the test error for the binders followed the specifications of Chinese Standard GB/T 8899-1998.

Table 5 Volume fraction of detected binders

Concentration of binder (%)

Section*

Volume fraction calculated (%)

Volume fraction observed (%)

\(\frac{\text{Observed}}{\text{Calculated}}(\% )\)

3

C

1.60

0.845

52.8

5

C

2.65

1.108

41.8

L

1.335

50.4

7

C

3.67

1.986

54.1

L

1.796

48.9

9

C

4.67

2.223

47.6

L

2.082

44.6

As shown in Table 5, the observed binders accounted for about 50 % of the total volume fraction, so the agglomerated binders are present in the briquettes in similar proportions to the dispersed binders. Friction between the binder and the polishing machine can cause some binder to fall off during preparation of the polished sections. Agglomerated binders fall out more easily than dispersed binders. Greater amounts of the agglomerated binders fall out with amount  increasing of binder added, which accounts for the decreasing proportion of observed binder as the additive increases.

Distribution diagrams of the binders in briquettes are shown in Fig. 2 (agglomerated binders are shown as circles with equivalent areas while dispersed binders are neglected). The aggregated binders with large differences in size are not well-distributed, which indicates an inhomogeneous briquette microstructure. Larger size differences are found for the agglomerated binders as the binder concentrations increase.

Fig. 2
figure 2

Distribution diagrams of agglomerated binders in briquettes. The X and Y axes represent the two-dimensional coordinate system described in Sect. 2.2

3.2 Roundness of binders and its implications

Spheroid or laminated structures (Yu and Liu 1989), which would be ellipses in two-dimensions, are used to represent the minor microstructural components. The concept of roundness is introduced to characterize the binder morphology in this study. Roundness is defined as the ratio of the long axis to the short axis for the equivalent ellipse of the binder particles. If this ratio is in unity, then the roundness of the binder particle is 1. The roundness values of binders in different sections, made by using different quantities of binder, are shown in Fig. 3; the corresponding histogram is shown in Fig. 4.

Fig. 3
figure 3

Roundness of binders

Fig. 4
figure 4

Roundness histogram

As shown in Figs. 3 and 4, the binder roundness values are concentrated between 1.5 and 4.0, with a small fraction close to 1, and a few values above 4.0 in different sections of the briquettes with different binder concentrations. Bentonites in the longitudinal sections of briquettes with binder concentrations of 7 % and 9 % are more likely to have roundness values above 4.0. The roundness of bentonite free of compression is close to 1.0, as shown in Fig. 5, which indicates that the roundness changing is caused by the pressure that the binders are subjected to during briquetting.

Fig. 5
figure 5

Optical microscopy image of binders free of compression (reflected light, air, polarized light, ×100)

Most aggregated binders were compressed and conformed well to the surfaces of coal particles, with some binder particles changing shape when moving with the coal particles, thereby resulting in most binder roundness values between 1.5 and 4.0. Small quantities of the binders were subjected little pressure, so showed little change of morphology, and gave a roundness of approximate 1. The binders in the longitudinal section (compression section) of the briquettes with binder concentrations of 7 % and 9 % moved substantially and changed shape considerably, so these binders were more likely to have roundness values exceeding 4.0. Large-sized agglomerated binders, which experienced large morphology changes during compression, are found in briquettes comprising large amount of binders.

3.3 The influences of binder morphology and distribution on briquette strength

The compressive strength, impact strength, and thermal stability of briquettes made with different binder concentrations are listed in Table 6. The relationships between briquette strength and binder concentration are shown in Fig. 6. Poor compressive strength and impact strength were found in briquettes with only small amounts of bentonite binder added.

Table 6 Compressive strength, impact strength, and thermal stability of briquettes

Amount of binder (%)

Compressive strength (N/ball)

Impact strength (%)

Thermal stability (%)

TS+13

TS−3

3

105

27

75.1

16.9

5

115

32

75.8

16.5

7

202

48

84.5

10.7

9

195

45

89.3

6.6

Fig. 6
figure 6

Relationship between strength of briquettes and binder concentration. a Relationship between mechanical strength and concentrations of binder. b Relationship between thermal stability and concentrations of binder

The binders dispersed in the coal/binder matrix are believed to act as fully adhesive, which benefits the mechanical strength of the briquettes. The amounts of dispersed binders increased as the concentration of binder increased. Large, unevenly distributed, agglomerated particles of binders that shrank during the drying process can generate fractures in the spaces between the binders and the coal particles, which is harmful to the mechanical strength (Wang et al. 2013). A larger size difference was found for the agglomerated binders as the binder concentration increased. When small amounts of binder were used, the cohesiveness of the dispersed binders was the dominating factor, with small volumes of agglomerated binders in the briquettes, and so the mechanical strength of the briquettes increased as the binder concentration increased. When the binder concentration was high enough, the volumes of the agglomerated binders increased significantly and strength-controlling flaws were produced, so mechanical strength of the briquettes decreased as the binder concentration increased, as shown in Fig. 6a.

On the other hand, bentonites lose little mass at high temperatures, so large binder particles act as a “framework” in the briquettes, which is beneficial to their thermal stability (Xu and Liu 2001). Thermal stability increased with increasing binder concentration, as shown in Fig. 6b.

Because of the conflicting influences on mechanical strength and thermal stability due to agglomerated binders, only a limited amount of binder can be used. The aggregated binder components were detrimental to briquetting overall.

Binders with roundness approximating 1 (little pressure in briquetting) acted as neither agglomerated nor dispersed binders, so these were “useless” in briquettes. Further study is needed to reduce the proportion of these types of binders. Binders with roundness above 4.0 were usually overloaded, so were not always beneficial and there was an upper limit on the amount of bentonite that can be used.

4.Conclusions

The morphology and distribution of binders in briquettes and their influence on briquette strength were studied by optical microscopy and digital image processing, which indicated:

  1. (1)

    Aggregated and dispersed binders, which were present in similar proportions, are the major forms of binders in briquettes. Aggregated binders with large size differences are not well-distributed. Larger size differences are found for agglomerated binders as the binder concentration increases.

  2. (2)

    The concept of roundness is introduced to characterize the binder morphology and indicate the pressure experienced by the binder during briquetting. This showed that most binders with roundness values between 1.5 and 4.0 were compressed and conformed well to the interfaces of coal particles, while those subjected to little pressure had a roundness approximating 1.0. The binders in the compression direction changed shape substantially.

  3. (3)

    The morphology and distribution of the binders changed as the binder concentration increasing, thereby influencing the strength of the briquettes. Aggregated binders were detrimental to mechanical strength while dispersed binders benefited briquetting.

References

[1] GB/T 16773-2008 (2008). Method of preparing coal samples for coal petrographic analysis. Standards Press of China, Beijing
[2] Jiang GL, Zhang PP (2005) Processing and application of bentonite. Chemical Industry Press, Beijing
[3] Liu JJ, Zhou YP, Li SL (2001) Physical chemistry, 4th edn. Higher Education Press, Beijing
[4] Mehta PK, Monteiro PM (2006) Concrete: microstructures, properties and materials, 3rd edn. McGraw-Hill, New York
[5] MT/T 924-2004 (2004a). Determination of thermal stability of industrial briquette. China Coal Industry Publishing House, Beijing
[6] MT/T 925-2004 (2004b). Drop shatter test of industrial briquette. China Coal Industry Publishing House, Beijing
[7] MT/T 748-2007 (2007). Determination of cold compressive strength of industrial briquette. China Coal Industry Publishing House, Beijing
[8] Nan CW (2005) Physics of heterogeneous materials. Science Press, Beijing
[9] Olson GB (1997) Computational design of hierarchically structural materials. Science 277:1237–1242
[10] Richards SR (1990) Physical testing of fuel briquettes. Fuel Process Technol 25:89–100
[11] Stach E, Mackowsky M, Techmüller M, Taylor GH, Chandra D, Techmüller R (1982) Stach’s textbook of coal petrology (third edition). Gebrüder Borntraeger, Berlin
[12] Wang Y, Bai XF, Wang DS et al (2013) Optical microscopic analysis of factors influencing cold strength of briquettes. Coal Convers 36(2):79–82
[13] Xu SL (2011) Fracture mechanics of concrete. Science Press, Beijing
[14] Xu ZG, Liu SQ (2001) Briquetting technology. China Coal Industry Publishing House, Beijing
[15] Yu NN, Liu GQ (1989) Stereology. Metallurgical Industry Press, Beijing
[16] Zeng F, Hu YP, Yang Y, Ren SZ, Yang YF (2001) Particle technology of mineral processing. China University of Mining and Technology Press, Xuzhou

About this article

Cite this article

Wang, Y., Bai, X. Optical microscopy analysis of briquette binders.Int J Coal Sci Technol 1, 421–427 (2014).
  • Received

    10 March 2014

  • Revised

    01 December 2014

  • Accepted

    02 December 2014

  • Issue Date

    December 2014

  • DOI

    https://doi.org/10.1007/s40789-015-0051-8